Non-isothermal creep age forming of Al-Cu-Li alloy: Experiment and modelling

Non-isothermal Creep Age Forming (CAF), including loading, heating, holding, cooling and springback stages, is an advanced forming technique for manufacturing high performance large integral panels at short production period and low cost. However, the creep deformation and aging precipitation during heating stage is often neglected in experiments and modeling, leading to low forming precision. To achieve shape forming and property tailoring simultaneously, a deep understanding of the non-isothermal creep aging behavior and the establishment of predictive models are urgently required. A new five-stage creep feature of Al-Cu-Li alloy during the non-isothermal creep aging is observed. The microstructural interactions between the dislocations, solute atoms, Guinier Preston zones (GP zones) and T₁ precipitates are found to dominate the five-stage creep aging behavior. The physical-based model considering temperature evolution history is established to describe the five-stage creep feature. The springback and yield strength of non-isothermal creep age formed plates with different thicknesses are predicted and compared by non-isothermal CAF experiments and corresponding simulations. The CAF experiments show that the springback and yield strength of the non-isothermal creep age formed plate are 62.1% and 506 MPa, respectively. Simulation results are in good agreement with experimental results. The proposed model broadens the application of traditional CAF models that mainly focus on isothermal conditions.     

Effect of adding Nb foil on joint properties of laser fusion welding for TC4 titanium and 7075 aluminum alloy

It is difficult to gain effective Ti-Al fusion welding joints due to their differences in thermal properties and the appearance of brittle Ti-Al Intermetallic Compounds (IMCs). The experiments of laser fusion welding for TC4 titanium and 7075 aluminum alloy were carried out, temperature field and ductility/brittleness, as well as chemical potential of elements, were calculated, and the effect of adding Nb foil on mechanical properties of the weld was also investigated. The results suggested that Nb atoms tend to diffuse toward Al side, which is conducive to the participation of Nb in the metallurgical reaction and contributes to forming the Ti-Nb-Al IMC layer at the interface. As the thickness of Nb foil increases, the tensile-shear force of joint climbs first but then declines, and reaches the highest value of 1663 N with 0.10 mm-thickness Nb foil, representing 58.38% enhancement compared with the non-added one. Adding Nb foil slows down the heat transfer as a blocker, and thus both the melting amount of Al and the mixing area of Ti and Al decrease. In addition, Nb alloying reduces the brittleness of the Ti-Al compound. Hence, the joint properties of titanium/aluminum are improved with the addition of Nb foil.     

拉伸载荷下正交三向机织复合材料接头失效多尺度渐进损伤分析

针对机械打孔三维机织复合材料耳片接头的单轴拉伸破坏性能，采用多尺度分析方法研究孔边纱线破坏过程。结果表明，正交三向（ORT）机织复合材料接头孔边的连续的经纱出现大量的纵向损伤；纬纱单元出现大量横向损伤，损伤沿着孔边45°方向逐渐扩展，纬纱发生剪切失效，最终接头的损伤形式为剪切破坏。数值模拟和试验结果的误差为1.14％，验证了多尺度有限元仿真方法的正确性。孔边细观区域的纱线损伤从孔边扩展到边接头边缘。孔边纱线的分布位置不同，纱线的破坏形式虽不一样，但是不影响破坏的扩展趋势。     

复合材料面板阻燃抗菌防霉性能

采用热熔法制备抗菌防霉预浸料,并对其力学性能、燃烧产物、阻燃性能以及抗菌防霉性能进行了系统的评价。结果表明:复合材料面板的燃烧产物中CO、HF、HCl、NOx、SO2、HCN等6种毒性气体含量均远远低于标准;阻燃性能优异,无火焰穿透,无熔融物滴落,且平均自熄时间大都为0 s;防霉性能均为0级;抗菌性能随着抗菌防霉剂含量的增大而增强,其中当抗菌防霉剂含量≥2%性能随着抗菌防霉剂的添加呈下降趋势,为了兼顾力学性能与抗菌性能,创新设计不同抗菌防霉剂分布而保持平均含量不变的复合材料面板,对比抗菌性能结果发现将抗菌防霉剂含量高的预浸料分布在表面时得到的复合材料面板拥有最优异的抗菌性能,成功实现结构生物安全一体化。     

C/SiC-SiO_(2)复合材料的制备及性能研究北大核心CSCD

采用溶胶凝胶和前驱体浸渍裂解混合工艺,制得了不同SiO_(2)/SiC比例的C/SiC-SiO_(2)复合材料,研究了SiO_(2)添加量对复合材料微观结构、力学性能的影响。结果表明:当添加SiO_(2)的质量分数约25%时,材料的拉伸强度和压缩强度与C/SiC材料性能相当;而当添加SiO_(2)的质量分数超过25%时,材料的强度与模量均随SiO_(2)含量的增加呈降低趋势。此外,SiO_(2)含量约25%的C/SiC-SiO_(2)复合材料的浸渍相成本较C/SiC材料降低约24%左右,这为C/SiC复合材料的快速低成本制备提供了新的技术支撑。     

A novel combination belief rule base model for mechanical equipment fault diagnosis

Due to the excellent performance in complex systems modeling under small samples and uncertainty, Belief Rule Base(BRB) expert system has been widely applied in fault diagnosis. However, the fault diagnosis process for complex mechanical equipment normally needs multiple attributes, which can lead to the rule number explosion problem in BRB, and limit the efficiency and accuracy. To solve this problem, a novel Combination Belief Rule Base(C-BRB) model based on Directed Acyclic Graph(DAG) structu...     

2195铝锂合金钨极氩弧焊接工艺研究

针对2195铝锂合金在焊接时裂纹敏感性高、气孔敏感性高、易氧化等问题，开展氩弧焊接工艺研究，对焊接头的抗裂性、力学性能及显微组织进行了分析。研究表明，提高焊缝金属中的Cu含量，可以有效降低2195铝锂合金熔焊接头的裂纹敏感性，裂纹率K₁=0%,K₂=0%。2195铝锂合金单面双层焊接接头力学性能最佳，抗拉强度超过376 MPa，延伸率达到5.5%。提高焊接试板的清理深度可以解决焊接气孔敏感性高的问题，增加氩气拖后保护及背保护措施可以有效防止焊接氧化问题。熔焊工艺研究可为2195铝锂合金的工程应用提供技术支撑。     

2219 T852过渡环与T87箱筒段电子束焊接接头性能

基于贮箱用2219 T852整体过渡环与T87箱筒段的电子束环焊缝,开展了部段级电子束焊接接头常、低温力学性能测试,同时对焊接接头错缝量、断裂类型及金相组织进行了分析。研究结果表明:部段级常、低温2219 T852与T87电子束焊接接头的强度影响系数为0.63,低温状态下焊接接头的力学性能比室温状态下有所提高;错缝量与焊接接头力学性能成反比,其中对延伸率影响最为显著,低温有助于缓解错缝对焊接接头力学性能的弱化影响;电子束焊接接头组织不均匀性和结构形貌上的不连续性,特别是T852侧热影响区晶粒粗大,导致T852侧热影响区和焊缝接头根部为电子束焊缝的薄弱区域,焊接接头极易在该区域发生断裂。     

TiB2颗粒对2195铝锂合金焊接头焊接性的影响

为了解决2195铝锂合金在焊接时裂纹敏感性高、焊接头软化等问题,通过调整焊丝的化学成分,添加微米级原位自生TiB_2颗粒,制备出BJ-4210焊丝,并对焊接头的抗裂性、力学性能及显微组织进行了研究。研究表明,TiB_2颗粒在熔池中作为形核质点,能够降低焊缝晶粒尺寸并且改变晶粒形态,从而有效的降低接头的裂纹敏感性,提高接头的力学性能,其拉伸强度达到370 MPa,延伸率为3.1%。BJ-4210焊丝的研制可为2195铝锂合金的工程应用提供技术支撑。     

深空极低温服役环境下材料力学/物理性能低成本快速评价方法研究进展

随着我国空间探测卫星、深空探测飞行器等国家战略装备的快速发展,宇航材料的服役环境越来越苛刻,常常面临极端低温的考验。然而低温下材料的力学/物理性能和常温相比有很大差异,极低温使役环境下材料力学/物理性能评价成为人们关注的重点问题。本文着重对基于力-热能量密度等效原理而发展的深空极低温服役环境下材料屈服强度、弹性模量、理想拉伸强度、硬度等力学性能的低成本快速评价方法研究进展进行了总结和回顾;同时,介绍了力-热能量密度等效原理在低温下半导体材料的带隙能、折射率、拉曼频移,金属材料磁晶各向异性常数等物理性能的低成本快速评价方面的推广应用情况。该评价方法为实现地面实时监测在轨航天器中关键材料的主要力学/物理性能提供了有效途径,为国家高端技术装备建设中关键材料的设计、可靠性评价和实时性能监测等提供重要的手段。